The weld bead of the automatic welding equipment is generally white and bright. However, if the use method is incorrect, it may also lead to black after welding. If the automatic welding equipment is black after welding, the possible reasons are:

1、氬氣沒(méi)有打開(kāi)或者氣罐內(nèi)已經(jīng)沒(méi)有氬氣，需要檢查氬氣瓶閥門(mén)和氬氣表開(kāi)關(guān)。

1. If the argon is not opened or there is no argon in the gas tank, check the valve of the argon cylinder and the switch of the argon meter.

2、鎢針露出陶瓷嘴距離太長(zhǎng)，在焊接過(guò)程中氬氣并沒(méi)有起到防氧化作用。

2. The distance between the tungsten needle and the ceramic nozzle is too long, so argon does not play an anti oxidation role in the welding process.

3、自動(dòng)焊接設(shè)備的參數(shù)調(diào)節(jié)過(guò)大，沒(méi)有按照工況調(diào)節(jié)相應(yīng)的材料及厚度所應(yīng)設(shè)置的電流大小及放弧時(shí)間。

3. The parameter adjustment of automatic welding equipment is too large, and the current size and arcing time that should be set for the corresponding material and thickness are not adjusted according to the working conditions.

4、工件表面雜質(zhì)過(guò)多，沒(méi)有提前清理工件表面的油污、氧化物等雜質(zhì)。

4. There are too many impurities on the surface of the workpiece, and the impurities such as oil and oxide on the surface of the workpiece are not cleaned in advance.

5、工件工藝要求過(guò)高，該型號(hào)的自動(dòng)焊接設(shè)備配置不足，無(wú)法完成焊接需求。

5. Workpiece process requirements are too high, and the automatic welding equipment of this model is insufficient to meet the welding requirements.

怎么操作不發(fā)黑？

How to operate without blackening?

1、選擇符合工件加工需求的山東自動(dòng)焊接設(shè)備配置，并根據(jù)弓箭情況調(diào)節(jié)好相應(yīng)的參數(shù)。

1. Select the automatic welding equipment configuration that meets the workpiece processing requirements, and adjust the corresponding parameters according to the bow and arrow conditions.

2、在焊接的時(shí)候，要選擇合適的焊絲，所填焊絲直徑好小于工件厚度。

2. When welding, select the appropriate welding wire, and the diameter of the filled welding wire is better than the thickness of the workpiece.

3、焊接時(shí)，應(yīng)盡量減小工件之間的焊縫距離，焊縫盡量清理干凈。

3. During welding, the weld distance between workpieces shall be minimized and the weld shall be cleaned as much as possible.

4、焊接到末端后停留一秒左右，千萬(wàn)別立刻移開(kāi)焊槍，防止后焊點(diǎn)氧化。

4. Stay for about one second after welding to the end. Never remove the welding gun immediately to prevent oxidation of the rear welding spot.

自動(dòng)焊接設(shè)備焊出來(lái)發(fā)黑是什么原因已經(jīng)講解完畢了，當(dāng)然處理措施我們也列出來(lái)了，給您好的參考信息。更多相關(guān)事項(xiàng)就來(lái)我們網(wǎng)站http://www.camtask.com咨詢吧！

The reason why the automatic welding equipment blackens after welding has been explained. Of course, we have also listed the treatment measures for your reference. Come to our website for more information http://www.camtask.com Consult!